Home > products > Honeycomb Ceramic > Oval Honeycomb Ceramic

Oval Honeycomb Ceramic

Category:
Honeycomb Ceramic
Payment Method:
T/T, L/C
Specifications
Cells Density::
100~600 CPSI
Material::
Cordierite
Size::
Customize
Color::
White
Name::
Catalyst Substrates, Catalyst Supports, Ceramic Honeycomb
Shape::
Round
Usage::
Exhaust Gas Purification
High Light:

ceramic catalytic converter

,

ceramic catalyst support

Introduction

Oval Honeycomb Ceramic Carrier White For Exhaust Gas Purification
 

 

2.   1.Product use

 After coated with catalysts, this product is applied in catalytic converter of gasoline vehicle to catalyze, convert and purify the exhaust, making vehicle exhaust reaching standards of Euro IV and Euro V.

 

2.Overall dimensions standards

 

Item

Standard value

Tolerance range

Remark

wall thickness

0.17MM

+0.03MM

-0.02MM

 

density scope

440g/L

±60g/L

 

Outside dimension

≤100MM

±1MM

 

>100MM

±1%

 

Perpendicularity

 ≤100MM

≤1%height

 

Parallelism

 >100MM

≤1%height

 

 

Physical and chemical properties

 

Item

Standard value

Inspection Method

chemical components

Al2O3

35.2±1%

Chemical analysis

SiO2

50.9±1%

MgO

13.9±1%

Cordierite Crystal phase

≥90%

X-ray diffraction techniques

Compressive

strength

AA xis

≥15 Mpa

Compressive strength technique

BA xis

≥2 Mpa

CA xis

≥0.15 Mpa

Water absorption

20-26%

 

Weighting methord

Softening point

≥1400

High temperature oven

CTE(800℃)

≤1.2*10-6/℃

Netzsch dil 402  PC

Thermal shock resistance

550℃three times(air cool)

Muffle furnace

 

 

Description:

 

After coated with catalysts, this product is applied in catalytic converter of gasoline vehicle to catalyze, convert and purify the exhaust, making vehicle exhaust reaching standards of Euro IV and Euro V.

Benefits of Products:

● Thin wall thickness

● Low pressure drop

● High surface area

● Height compressive strength

● Low thermal expansion coefficient

● Good thermal impact resistance and thermal shock resistance

● Excellent compatibility with various active composition in catalyst

●Good performance in cold start, low ignition temperature, quick temperature rise, little air resistance, and high conversion efficiency.

 

 

Applications:

 

    After coated with catalysts, this product is applied in catalytic converter of gasoline vehicle to catalyze, convert and purify the exhaust, making vehicle exhaust reaching standards of Euro IV and Euro V. Technical performance of this product has achieved advanced level in China, and it approaches or has already reached the advanced level of similar products abroad.

 

 

Specifications

 

Cell density (CPSI):100~600

 

Item

(mm)

Sectional Dimension

(mm2)

Area of Section

 

Shape of Section

(mm)

Height

1

Φ76.2

4560

Oval Honeycomb Ceramic

≤200

The height can be designed by customer

(The standard height):76.2mm(3”), 101.6mm(4”), 127mm(5”),

152.4mm(6”).

2

Φ83

5410

Oval Honeycomb Ceramic

3

Φ93

6793

Oval Honeycomb Ceramic

4

Φ97

7390

Oval Honeycomb Ceramic

5

Φ101.6

8107

Oval Honeycomb Ceramic

6

Φ103

8332

Oval Honeycomb Ceramic

7

Φ105.7

8775

Oval Honeycomb Ceramic

8

Φ118.4

11010

Oval Honeycomb Ceramic

9

Φ144

16286

Oval Honeycomb Ceramic

10

80x57(R21.5)

3546

Oval Honeycomb Ceramic

11

99.5x68.1(R33.6)

5758

Oval Honeycomb Ceramic

12

120.6x80(R39.6)

8227

Oval Honeycomb Ceramic

13

144x68(R28.4)

8194

Oval Honeycomb Ceramic

14

144.3x68.1(R28.4)

8606

Oval Honeycomb Ceramic

15

144.8x81.3(R37)

9922

Oval Honeycomb Ceramic

16

147x95(R36.6)

11010

Oval Honeycomb Ceramic

17

148x84(R38)

10438

Oval Honeycomb Ceramic

18

169.7x80.8(R37.2)

11865

Oval Honeycomb Ceramic

19

Triangle

143.5×84

9108

Oval Honeycomb Ceramic

20

Trapezium 112.2×92×152.4

8788

Oval Honeycomb Ceramic

21

Trapezium

122.3x104.4

10336

Oval Honeycomb Ceramic

22

Rectangle

119.5x99.5

10529

Oval Honeycomb Ceramic

23

Special

114x105

9612

 

 
 
 

REMARK: The SIZE can be designed by customer

 

 

Competitive Advantage:

 

● Thin wall thickness

● Low pressure drop

● High surface area

● Height compressive strength

● Low thermal expansion coefficient

● Good thermal shock resistance

● Excellent compatibility with various active composition in catalyst

●Good performance in cold start, low ignition temperature, quick temperature rise, little air resistance, and high conversion efficiency.

 

 