Round MgO Selective Catalytic Reduction Converter Substrate

Round MgO Selective Catalytic Reduction Converter Substrate

  • High Light

    ceramic catalyst support

    ,

    honeycomb ceramic substrate

  • Place of Origin
    China.Yixing
  • Brand Name
    Yuxing
  • Certification
    ISO9001 TS/16949
  • Minimum Order Quantity
    No
  • Packaging Details
    Standard export packing
  • Delivery Time
    5 work days
  • Payment Terms
    T/T, L/C
  • Supply Ability
    6 million liter/year

Round MgO Selective Catalytic Reduction Converter Substrate

Round MgO Selective Catalytic Reduction Converter Substrate

 

 

Description:

Benefits of Products:

   ● Low thermal expansion coefficient

   ● High porosity of hole on the wall , good liquidity and uniform distribution

   ● High temperature resistance, chemical corrosion resistance, thermal shock resistance and thermal shock resistance is strong

   ●The pressure drop is small.

   ● Cold start performance is good, low light-off temperature, high conversion efficiency

 

 

     1.  Product use

 

After coated with catalysts, this product is applied in catalytic converter of diesel vehicle to catalyze, convert and purify the exhaust, making vehicle exhaust reaching standards of Euro IV and Euro V. Technical performance of the product in the leading position in domestic, close to or reach the advanced level of similar foreign product.

 

2.Overall dimensions standards

Item

 

Standard values

 

Test method

 

Wall thinkness

100CPSI

0.45MM±0.03

vernier caliper

200CPSI

0.36MM±0.03

vernier caliper

300CPSI

0.28MM±0.03

vernier caliper

400CPSI

0.21MM ±0.03

vernier caliper

Overall dimensions

OD:<100MM

±1.0MM

vernier caliper

            ≥100MM

±1%

vernier caliper

Height:<150

±1.0

vernier caliper

       ≥150

±1%Height

vernier caliper

Internal crack

 

 

Bright light perspective

 

Physical and chemical properties

 

Item

Standard value

Test methods

chemical

component

 

Al2O3

35.2%±1%

chemical

analysis

SiO2

50.9%±1%

MgO

13.9%±1%

Cordierite main crystalline phase content

≥90%

X-ray diffraction

Compressive

strength at

room

temperature

 

AA xis

≥15Mpa

universal material

 testing machine

 

BB xis

≥2Mpa

CC xis

≥0.15Mpa

water absorption

23-27%

Gravimetric method

softening temperature

 ≥1400℃

high-temperature electric resistance furnace

CTE(800℃)

≤1.5*10-6/℃

thermal dilatometer

thermal shock

resistance

450℃

Three times don't crack

air cooling

 

 

Specifications

 

Cell density (CPSI):100~400

 

Item

(mm)

Sectional Dimension

(mm2)

Area of Section

 

Shape of Section

(mm)

Height

1

144(4.66”)

16282

Round MgO Selective Catalytic Reduction Converter Substrate 0

 

 

The height can be designed by customer.

(The standard height):76.2mm(3”), 101.6mm(4”), 127mm(5”),

152.4mm(6”).

2

150

17671

Round MgO Selective Catalytic Reduction Converter Substrate 1

3

165(6.5”)

21382

Round MgO Selective Catalytic Reduction Converter Substrate 2

4

170

22698

Round MgO Selective Catalytic Reduction Converter Substrate 3

5

175

24052

Round MgO Selective Catalytic Reduction Converter Substrate 4

6

190(7.5”)

28352

Round MgO Selective Catalytic Reduction Converter Substrate 5

7

210

34636

Round MgO Selective Catalytic Reduction Converter Substrate 6

8

228(9”)

40828

Round MgO Selective Catalytic Reduction Converter Substrate 7

9

240(9.5”)

45238

Round MgO Selective Catalytic Reduction Converter Substrate 8

10

267(10.5”)

55990

Round MgO Selective Catalytic Reduction Converter Substrate 9

11

286(11.25”)

64242

Round MgO Selective Catalytic Reduction Converter Substrate 10

12

305(12”)

73061

Round MgO Selective Catalytic Reduction Converter Substrate 11

13

330(13”)

85529

Round MgO Selective Catalytic Reduction Converter Substrate 12

 

 

 

REMARK: The SIZE can be designed by customer

 

 

Competitive Advantage:

 

  ● Low thermal expansion coefficient

  ● High porosity of hole on the wall , good liquidity and uniform distribution

  ● High temperature resistance, chemical corrosion resistance, thermal shock resistance and thermal shock resistance is strong

  ●The pressure drop is small.

  ● Cold start performance is good, low light-off temperature, high conversion efficiency